Hashemi Milani S A A, Tavangar R, Azadbeh M, Kahinpoor I, Sadeghi-Nasab H. Effect of NOCOLOK® Flux Dry-off Temperature on Mechanical Properties of Brazed Joint of Automotive Aluminum-Based Heat Exchangers. ASE 2020; 10 (4) :3381-3393
URL: http://www.iust.ac.ir/ijae/article-1-521-fa.html
Effect of NOCOLOK® Flux Dry-off Temperature on Mechanical Properties of Brazed Joint of Automotive Aluminum-Based Heat Exchangers. Automotive Science and Engineering. 1399; 10 (4) :3381-3393

URL: http://www.iust.ac.ir/ijae/article-1-521-fa.html


چکیده:   (5370 مشاهده)
Drying temperature of the flux at normal atmosphere has a crucial role in brazing quality in automotive aluminum-based heat exchangers. Over the course of this research, NOCOLOK® flux consists of two phases of K2AlF5.H2O and KAlF4 with melting point around 580 °C was used. A flux slurry was applied on the base metal, and dried at 220, 300 and 380 °C in air. Mechanical assessment revealed that when flux dried at 300 °C, the joint withstands maximum shear stress of 44 MPa with complete bonding. At 220 °C and 380 °C, joint shear stresses are 34 MPa, 30 MPa respectively. 380 °C dry-off temperature under nitrogen gas improved shear strength to 39 MPa. Taking dry-off temperature as 300 °C the amount of defective heat exchangers was reduced from 6% to 2% on a daily basis.
 
متن کامل [PDF 999 kb]   (5494 دریافت)    
نوع مطالعه: پژوهشي | موضوع مقاله: ساخت

ارسال نظر درباره این مقاله : نام کاربری یا پست الکترونیک شما:
CAPTCHA

بازنشر اطلاعات
Creative Commons License این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است.

کلیه حقوق این وب سایت متعلق به مجله بین‌المللی مهندسی خودرو می باشد.

طراحی و برنامه نویسی : یکتاوب افزار شرق

© 2024 CC BY-NC 4.0 | Automotive Science and Engineering

Designed & Developed by : Yektaweb