Ogbonna V, Olayiwola P, Mgbemere H. Effect of Varying Silicon Carbide Particulate on the Mechanical Properties of Aluminium Based Alloy Automobile Brake Disc Component. ASE 2019; 9 (2) :2934-2941
URL: http://www.iust.ac.ir/ijae/article-1-504-fa.html
URL: http://www.iust.ac.ir/ijae/article-1-504-fa.html
Effect of Varying Silicon Carbide Particulate on the Mechanical Properties of Aluminium Based Alloy Automobile Brake Disc Component. Automotive Science and Engineering. 1398; 9 (2) :2934-2941
چکیده: (14875 مشاهده)
In the current study, effect of varying Silicon Carbide particulate on the mechanical properties of Aluminium based alloy automobile brake disc component was investigated. The result of experimental investigation on mechanical properties of Silicon Carbide particle reinforced Aluminium Matrix was achieved for composite brake disc using universal tensile test machine, Rockwell hardness testing machine and numerical/theoretical model. The influence of reinforced ratio of 5, 10, 15 20, and 25 weight percentage of Silicon Carbide particles on mechanical properties was examined. Aluminium Metal Matrix Composites containing, 5, 10, 15, 20, and 25 weight percentages of reinforcement Particles was obtained using Stir-Casting method. The result obtained showed that highest Yield Strength (350.64MPa), Modulus of Rigidity (6137.4MPa), and Hardness (76.5Kg/mm2) was obtained on 25wt%SiC (190μm) particle reinforcements.